杉木和I-72杨人工林木材干缩性质的研究

通过对杉木和I-72杨人工林木材南北向、不同高度位置、不同径向位置横向干缩(弦、径向)的测量,研究上述3个因素对2种木材横向干缩(弦、径向)的影响规律。结果表明:南北向的不同对杉木和I-72杨人工林木材的干缩均无显著影响;高度位置的不同对杉木和I-72杨木的弦向干缩均有显著影响,而对径向干缩则无显著影响;径向位置的不同对杉木和I-72杨人工林木材的径、弦向干缩均有极显著影响:从树皮到髓心,木材径、弦向干缩逐渐减小,与其基本密度的变化趋势一致。     

红松幼龄材与成熟材力学性质的差异

本文研究了人工林和天然林红松幼龄材与成熟材力学性质的差异.结果显示,成熟材的所有力学性质均高于幼龄材.幼龄材与成熟材的抗弯弹性模量差异在人工林红松中达0.01水平显著,天然林红松也达到0.01水平显著;人工林红松抗弯强度和弦向横纹抗压强度差异达0.05水平显著.抗弯强度、顺纹抗压强度、横切面硬度和弦向横纹抗压强度4项指标的差异达0.05水平显著.     

The influences of boiling and drying treatments on the behaviors of tension wood with gelatinous layers in <Emphasis Type="Italic">Zelkova serrata</Emphasis>

This study examined how boiling and drying treatments influenced various physical properties of the tension wood with gelatinous fibers (G-fibers) of a 29-yearold Zelkova branch. By boiling treatment, tension wood with numerous G-fibers contracted considerably in the longitudinal direction and the longitudinal Young’s modulus decreased in spite of the water-saturated condition. The drying treatment caused green tension wood and boiled tension wood with numerous G-fibers to shrink longitudinally and increased their longitudinal Young’s moduli. These specific behaviors in tension wood were highly correlated with the proportion of G-fibers in a specimen and were probably caused by the microscopic behavior of cellulose microfibril (CMF) in the gelatinous layers (G-layers). The longitudinal shrinkage of tension wood due to drying suggests the existence of a hygro-sensible, noncrystalline region in the CMF, which is abundant in the G-layer. Furthermore, the noncrystalline region in the CMF softens during boiling treatment, resulting in the reduction of the longitudinal Young’s modulus in tension wood. The longitudinal contraction of tension wood with G-fibers by boiling might be caused by the tensile growth stress remaining in green G-layers. However, no changes were detected in the 004 d-spacing of cellulose crystal in tension wood from the boiling and drying treatments, regardless of the proportion of G-fibers.     

不同立地条件香椿人工林木材材质的比较

通过对不同立地条件下香椿人工林木材物理力学性质的测定和比较分析表明:香椿人工林木材密度和干缩性随着立地级的提高而减小;木材顺纹抗压强度、抗弯强度和硬度:Ⅰ级地<Ⅱ级地<Ⅲ级地,抗弯弹性模量、抗劈力、冲击韧性:Ⅱ级地>Ⅰ级地>Ⅲ级地,顺纹抗剪强度:Ⅱ级地>Ⅲ级地>Ⅰ级地。差异显著性t检验表明:香椿人工林木材密度Ⅰ级地、Ⅱ级地、Ⅲ级地间差异不显著。香椿人工林木材干缩性和力学性质指标Ⅰ级、Ⅱ级、Ⅲ级地3者间有的指标差异极显著,有的指标差异显著,大部分指标差异不显著。     

人工林软质木材表面密实化新技术

采用一种新型木材改性处理剂，分别以改性异氰酸酯浓度5％、10％、15％、20％，对美国人工林火炬松（Pinus taeda）进行表面密实化处理。结果表明，随着树脂浓度的增加，无论是冷水浸泡还是煮沸，木材的吸水厚度膨胀率和压缩变形恢复率明显降低。表面密实化后，火炬松处理材的MOR和MOE值分别比素材提高43．9％和30．1％；水浸24h和煮沸2h后的湿状抗弯性能比素材略低，干状抗弯性能明显比素材高，MOR分别高28．0％和25．76％；MOE分别高22．55％和27．79％。改性异氰酸酯浸渍处理后的表面密实化木材，具有一定的阻燃效果；表面耐磨耗性能和表面硬度亦明显改善。     

Influence of Ammoniacal Copper Quaternary treatments on mechanical properties of blue-stained Lodgepole Pine wood

Three concentrations （2.8%, 2.0%, 1.2%） of Ammoniacal Copper Quaternary （ACQ） was selected to treat Lodgepole pine wood for evaluating ACQ treatment on mechanical properties of blue-stained wood. The bending modules of elasticity （MOE）, modules of rupture （MOR）, toughness and shearing strength parallel to grain on tangential surface, are tested according to the criteria GB1927-1943-91. Non-treated sample were also tested according to the same procedure. The results showed that the three groups specimen impregnated by different concentrations of ACQ solution met the AWPA standard 2003 of America （UC4A 6.4g/cm^3）. There were significant difference of toughness between treated wood and non-treated wood （p=0.01）, but there were no statistically significant differences among three concentrations in terms of toughness, and toughness of treated wood was approximately 20% lower than non-treated. MOR, MOE as well as sheafing strength parallel to grain were found to be not significantly different between treated wood and non-treated one, and there were no statistically significant difference among three concentrations of ACQ too. Toughness, MOR, MOE and sheafing strength parallel to grain increased with decrease of concentration of ACQ, but they were hardly affected by ACQ preservatives.     

用活性染料对泡桐单板仿红木进行染色的影响因素

采用活性染料对预处理后的泡桐单板进行了仿红木染色研究.结果表明:活性染料对泡桐有较好的易染性,泡桐单板经染色后能达到红木商业用材的自然效果;活性染料染色时,由于上染和固色是分开进行的,固色前染料可以充分进行扩散移染,从而有效避免泡桐单板表芯色差现象;通过控制染色温度、时间以及促染剂和固色剂用量,可得到满意的染色效果.试验得出的染色工艺条件为:温度70~80℃,时间3 h,促染剂元明粉40 g/L,固色剂纯碱20 g/L.     

桉材热处理及其渗透性能的改善

本文以高温软化和瞬时降压之方法对三种桉材（Ｅｕｃａｌｙｐｔｕｓ）进行了汽蒸热处理试验。结果表明：除赤桉（Ｅ·Ｃａｍａｌｄｕｌｅｎｓｉｓ）外，热处理后的桉材导管壁上纹孔膜出现了不同程度的破裂，甚至脱落为空洞。其渗透性能得到了较明显的改善。其中以１４０℃、５ｈ的热处理效果为佳。     

杨木和杉木木材表面性质的研究

以人工林杨木和杉木木材为研究对象 ,对其表面自由能、表面极性和表面化学官能团等木材表面特征因子进行测定 ,并探讨不同温度处理条件下木材表面特性的变化机理。研究结果表明 :杉木比杨木有较高的总表面自由能 (42 35mN·m- 1 对 38 93mN·m- 1 )和非极性表面自由能 (41 6 1mN·m- 1 对 35 5 2mN·m- 1 ) ,而杨木的极性表面自由能比杉木要高 (3 4 1mN·m- 1 对 0 74mN·m- 1 )。杨木和杉木木材经过不同温度处理后 ,其总表面自由能和非极性表面自由能都随着处理温度的升高而下降 ,而极性自由能则有不同程度的升高。产生此种现象的原因主要为木材表面羟基缔合状态的解除及表面脱羟基作用的综合结果。木材表面 3种主要化学官能团为羟基、烷基和缩醛基 ,在高温处理条件下 ,两种木材羟基对烷基和缩醛基吸收峰面积之比都有所下降 ,说明高温处理过程是一个使木材表面羟基密度减少的过程。木材表面自由能与木材表面化学官能团变化有明显的相关性。     

人工林场杨木材性质与生长培育关系的研究

本文以生长在 3种长江滩地类型 (江滩、洲滩、湖滩 )、3种栽植密度 ( 3m×4m ,4m× 5m ,5m× 6m)下的3个品系速生人工林杨树木材 [欧美杨无性系 72杨 (Populus×euramericacv.I -72 58) ,美洲黑杨无性系 63杨(P .deltiodescv.I-63 51 )和 69杨 (P .deltoidescv.I-69 55) ,以下简称 72杨 ,63杨 ,69杨 ]为对象 ,深入地分析了人工林杨树木材材性与生长培育之间的关系。结果表明 :( 1 )品系对滩地杨树木材材性有较大的影响。安徽新洲洲滩和湖北黄洲江滩上生长的 63杨 ,湖南沅江湖滩上生长的 72杨纤维长度最长 ,微纤丝角最小 ,导管比量最大 ,方差分析表明 :72、63、69杨微纤丝角和主要物理力学性质差异均达显著和极显著。 ( 2 )滩地类型对72、63、69杨木材材性都有或大或小的差异。方差分析表明 :63杨、69杨微纤丝角、基本密度、抗弯强度和干缩率差异显著 ,说明 63杨和 69杨受滩地类型影响较大。 ( 3)栽植密度对 72、63、69杨木材材性的影响因材性指标的不同而不同。对 72、63、69杨来讲 ,栽植密度越大 ,微纤丝角、导管比量增大 ,纤维长度、木纤维比量、木射线比量都减小 ,基本密度、抗弯弹性模量和抗弯强度也越小。方差分析表明 ,72杨和 69杨受栽植密度影响较大 ,63杨受栽植密度影响较小